41Cr4
EN 10083-3:2002, Number: 1.7035
|
|
Comparasion of steel grades
|
|
JUS C.B9.021
|
Č.4131
|
|
DIN 17200
|
41Cr4
|
|
BS
|
530A40, 530M40
|
|
GOST
|
40H
|
|
AISI
|
5140H, A322
|
|
UNI
|
41Cr4
|
|
NF
|
41Cr4 42C4
|
Chemical analysis -% by mass
|
Chemical elements
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
-
|
|
%, by mass
|
0,38 - 0,45
|
£ 0,40
|
0,60 - 0,90
|
max 0.025
|
max. 0,035
|
0,90-1,20
|
-
|
|
Permissible deviation
|
± 0.02
|
± 0,03
|
± 0,04
|
+ 0.005
|
+ 0.005
|
± 0.05
|
-
|
Mechanical properties in the
quenched and tempered condition
|
|
d ≤ 16mm oder
t ≤ 8mm
|
16mm < d ≤ 40mm
8mm < t ≤
20mm
|
40mm < d ≤
100mm
20mm < t ≤
60mm
|
100mm < d
≤ 160mm
60mm < t ≤
100mm
|
160mm < d ≤
250mm
100mm < t
≤ 160mm
|
|
Re min (MPa)
|
800
|
660
|
560
|
-
|
-
|
|
Rm (MPa)
|
1000-1200
|
900-1100
|
800-950
|
-
|
-
|
|
A min. (%)
|
11
|
12
|
14
|
-
|
-
|
|
Z min. (%)
|
30
|
35
|
40
|
-
|
-
|
|
KV min. (J)
|
30
|
35
|
35
|
-
|
-
|
Jominy’s hardenability band
|
Distance in mm from quenched end
Hardness in HRC
(mm)
|
|
mm
|
1,5
|
3
|
5
|
7
|
9
|
11
|
13
|
15
|
20
|
25
|
30
|
35
|
40
|
45
|
50
|
|
+H
|
max.
|
61
|
61
|
60
|
59
|
58
|
56
|
54
|
52
|
46
|
42
|
40
|
38
|
37
|
36
|
35
|
|
min.
|
53
|
52
|
50
|
47
|
41
|
37
|
34
|
32
|
29
|
26
|
23
|
21
|
-
|
-
|
-
|
|
+HH*
|
max.
|
61
|
61
|
60
|
59
|
58
|
56
|
54
|
52
|
46
|
42
|
40
|
38
|
37
|
36
|
35
|
|
min.
|
56
|
55
|
53
|
51
|
47
|
43
|
41
|
39
|
35
|
31
|
29
|
27
|
26
|
25
|
24
|
|
+HL*
|
max.
|
58
|
58
|
57
|
55
|
52
|
50
|
47
|
45
|
40
|
37
|
34
|
32
|
31
|
30
|
29
|
|
min.
|
53
|
52
|
50
|
47
|
41
|
37
|
34
|
32
|
29
|
26
|
23
|
21
|
-
|
-
|
-
|
Heat treatment conditions –
informative
|
Hardening temperature
in the end quench test
|
Quenching temperature
|
Quenching in
|
Tempering temperature
|
|
8500±50C
|
820-860 0C
|
Oil or water
|
540-680 0C
|
Maximum hardness for products to be
supplied in the ’’treated to improve shearability (+S)’’ or
’’soft annealed (+A)’’ condition
|
+S
HB max.
|
+A
HB max.
|
|
255
|
241
|
|
41Cr4
EN 10250-3:1999, Number: 1.7035
|
|
Comparison of steel grades
|
|
JUS
|
Č.4131
|
|
DIN
|
41Cr4
|
|
BS
|
530A40, 530M40
|
|
GOST
|
40H
|
|
AISI
|
A322, 5140
|
|
UNI
|
41Cr4
|
|
NF
|
41Cr4, 42C4
|
Chemical analysis -% by mass *
|
Chemical elements
|
C
|
Si
|
Mn
|
P
max.
|
S
max.
|
Cr
|
-
|
-
|
-
|
|
%, by mass
|
0,38- 0,45
|
£ 0,40
|
0,60 - 0,90
|
0.035
|
0.035
|
0,90-1,20
|
-
|
-
|
|
|
Permissible deviation
|
± 0.02
|
+ 0,03
|
± 0,04
|
+ 0.005
|
+ 0.005
|
± 0.05
|
-
|
-
|
-
|
* At
the option the manufacturer the elements aluminium, titanium, vanadium and
niobium may be added singly or in combination for grain control
purposes. Elements not quoted in tables shall not be added intentionally to
the steel without the agreement of the purchaser, except for the purpose
of finishing the heat.
Mechanical properties in the quenched and tempered condition
|
Trickness of ruling
section tR
|
|
Diameter in mm
|
≤ 70mm tR
(longitudinal)
|
70< tR
≤160mm
|
160<tR≤330mm
|
|
Re min (N/mm2)
|
560
|
-
|
-
|
|
Rm min (N/mm2)
|
800
|
-
|
-
|
|
A % min..
|
14
|
-
|
-
|
|
KV min (J)
|
35
|
-
|
-
|
Heat treatment conditions **
|
Quenching temperature,
0C
|
Tempering temperature, 0C
|
|
820 to 860
|
540 to 680
|
 |
|
|