28NiCrMoV8-5
EN 10250-3:1999, Number: 1.6932
|
|
Comparison of steel grades
|
|
JUS
|
-
|
|
DIN
|
28NiCrMoV8 5
|
|
BS
|
-
|
|
GOST
|
-
|
|
AISI
|
-
|
|
NF
|
-
|
Chemical analysis -% by mass *
|
Chemical elements
|
C
|
Si
|
Mn
|
P
max.
|
S
max.
|
Cr
|
Mo
|
Ni
|
V
|
|
%, by mass
|
0,24- 0,32
|
£ 0,40
|
0,15-0,40
|
0.035
|
0.035
|
1,00-1,50
|
0,35-0,55
|
1,80-2,10
|
0,05-0,15
|
|
Permissible deviation
|
± 0,02
|
+ 0,03
|
± 0,04
|
+ 0,005
|
+ 0,005
|
± 0,05
|
± 0,06
|
± 0,05
|
± 0,02
|
* At the option the manufacturer the elements aluminium,
titanium, vanadium and niobium may be added singly or in combination for grain
control
purposes. Elements not quoted in tables shall not be added
intentionally to the steel without the agreement of the purchaser, except for
the purpose
of finishing the heat.
Mechanical properties in the quenched and tempered condition
|
Thickness of ruling section tR
|
|
Diameter in mm
|
tR ≤ 160mm
|
|
160< tR ≤330mm
|
330<tR≤660mm
|
|
Re min. (N/mm2)
|
630
|
|
590
|
590
|
|
Rm min. (N/mm2)
|
800
|
|
750
|
750
|
|
A % min.
|
l-longitudinal
|
14
|
|
15
|
15
|
|
tr - transverse
|
10
|
|
11
|
11
|
|
KV min (J)
|
l-longitudinal
|
45
|
|
40
|
40
|
|
tr - transverse
|
25
|
|
21
|
21
|
1N/mm2=1MPa
Heat treatment conditions ****
|
Quenching temperature, 0C
|
Tempering temperature, 0C
|
|
830 to 870
|
550 to 850
|
**** Quenching from hardening
may be carried out in oil, water, or water based solutions. Caution should
be observed in the use of water as a
quenching medium
to avoid the risk of cracking the forgings |
 |
|
|