10NiCr5-4
EN 10084-1998, Number: 1.5805
|
|
Comparison of steel grades
|
|
JUS
|
-
|
|
DIN
|
-
|
|
BS
|
637M17
|
|
GOST
|
-
|
|
AISI
|
-
|
|
NF
|
10NC6
|
Chemical composition (cast analysis)
|
Chemical elements
|
C
|
Si
max
|
Mn
|
P
max.
|
S
|
Cr
|
Ni
|
-
|
|
%, by mass
|
0,07-0,12
|
0,40
|
0,60-0,90
|
0,035
|
≤ 0,035
|
0,90-1,20
|
1,20-1,50
|
|
|
Permissible deviation
|
± 0,02
|
+ 0,03
|
± 0,04
|
+ 0,005
|
+ 0,005
|
± 0,05
|
± 0,05
|
-
|
Hardness limits for steel
|
Hardness HRC at a distance from quenched end of test piece (in
milimetres) of
|
|
mm
|
1,5
|
3
|
5
|
7
|
9
|
11
|
13
|
15
|
20
|
25
|
30
|
35
|
40
|
45
|
50
|
|
+H
|
max.
|
41
|
39
|
37
|
34
|
32
|
30
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
min.
|
32
|
27
|
24
|
22
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
+HH
|
max.
|
41
|
39
|
37
|
34
|
32
|
30
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
min.
|
33
|
29
|
26
|
24
|
21
|
20
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
+HL
|
max.
|
38
|
35
|
32
|
30
|
27
|
25
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
min.
|
32
|
27
|
24
|
22
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
Hardness requirements for products delivered in the conditions ’’treated to
improve shearabilita’’ (+S), ’’anneled to maximum hardness requirements’’ (+A),
’’treated to hardness range’’ (+TH) or ’’treated to ferrite-pearlite structure
and hardness range’’ (+FP)
|
Brinell hardness in the condition
|
|
+S max.
|
+A max.
|
+TH
|
+FP
|
|
min.
|
max.
|
min.
|
max.
|
|
*
|
192
|
147
|
197
|
137
|
187
|
|
|
|
|
|
|
|
Non-metallic inclusions
Requirements for
microscopic degree of purity when tested in accordance with
DIN 50 602
(method K) (valid for oxidic non-metallic inclusions)
|
D (mm)
Bars Diameter d (mm)
|
K
Total characteristic value K (oxides) for the individual cast
|
|
140 < d 200
|
K 4 ≤ 50
|
|
100 < d ≤ 140
|
K 4 ≤ 45
|
|
70 < d ≤ 100
|
K 4 ≤ 40
|
|
35 < d ≤ 70
|
K 4 ≤ 35
|
|
17 < d ≤ 35
|
K 3 ≤ 40
|
|
8 < d ≤ 17
|
K 3 ≤ 30
|
|
d ≤ 8
|
K 2≤ 35
|
Conditions for heat treating test bars and treatment of the steels
|
End quenchh test
Quenching, 0C
|
Carbunnzing temperature, 0C
|
Core-hardening temperature, 0C
|
Case-hardening temperature, 0C
|
Tempering, 0C
|
|
880
|
875 to 925
|
830 to 860
|
780 to 810
|
150 to 200
|
|
 |
|
|